Puttapaite, Pb2Mn2+2ZnCr3+4O2(AsO4)4(OH)6·12H2O, is a new mineral from the Beltana deposit, Puttapa, Flinders Ranges, South Australia, Australia. It forms rosette-like aggregates to 50 micrometers across composed of diamond-shaped tablets to 45 micrometers in length and 5 micrometers in thickness. Crystals are flattened on {001} and the observed forms are {001} and {110}. The calculated density is 3.562 g/cm–3. Optically, puttapaite is biaxial (−) with α = 1.700(5), β = 1.720(5), γ = 1.730(5) and 2V (meas.) = 67(1)°. Electron microprobe analyses gave the empirical formula (based on 36 oxygen atoms pfu) Pb1.96(Mn2+1.52Ca0.28Sr0.22)Σ2.02(Zn0.40Mg0.39Cu0.15)Σ0.94(Cr3+2.89Al0.45Fe3+0.40,Mn3+0.26)Σ4.00O2[(AsO4)3.71(Cr6+O4)0.29]Σ4.00(OH)6.13·11.87H2O. Puttapaite is monoclinic, C2/m, with a = 12.405(3), b = 10.565(2), c = 12.311(3) Å, β = 106.06(3)°, V = 1550.4(6) Å3 and Z = 2.

The structure was solved using synchrotron single-crystal X-ray diffraction data and refined to R1 = 0.1189 on the basis of 915 observed reflections with F0 > 4σ(F0). Puttapaite has a unique structure that consists of M4O16 clusters that share corners with TO4 tetrahedra, which in turn share corners with M1 octahedra in the [010] direction. Clusters link in the [001] direction via corner sharing M2 octahedra to form sheets parallel to {100}. Pb anions lie between the sheets.

Ferriphoxite, [(NH4)2K(H2O)][Fe3+(HPO4)2(C2O4)], and carboferriphoxite, [(NH4)K(H2CO3)][Fe3+(HPO4)(H2PO4)(C2O4)], are new mineral species from the Rowley mine, Maricopa County, Arizona, USA. They occur with antipinite, aphthitalite, baryte, fluorite, hematite and quartz in an unusual bat-guano-related, post-mining assemblage. Ferriphoxite occurs as rectangular blades, up to ∼0.1 mm in length, typically forming sprays. Carboferriphoxite occurs as needles or blades, up to ∼0.2 mm in length, typically forming fan- and bowtie-like sprays. Both species are colourless with white streak, vitreous lustre, ∼2 Mohs hardness, brittle tenacity and splintery fracture. Ferriphoxite has three good cleavages ({100}, {010} and {001}) and carboferriphoxite has two good cleavages (probably {100} and {001}). Both species have a measured density of 2.14(2) g·cm–3. Ferriphoxite is biaxial (+) with α = 1.524(3), β = 1.560(3), γ = 1.608(3) and 2Vmeas. = 83.9(4)°. Carboferriphoxite is biaxial (+) with α = 1.525(3), β = 1.555(calc), γ = 1.630(3) and 2Vmeas. = 67(1)°. Electron probe microanalysis gave {[(NH4)2.13K0.87]Σ3.00(H2O)} {(Fe3+0.95Al0.05)Σ1.00(HPO4)2(C2O4)} for ferriphoxite and {[(NH4)1.12K0.88]Σ2.00(H2CO3)} {(Fe3+0.78Al0.22)Σ1.00(HPO4)(H2PO4)(C2O4)} for carboferriphoxite. Ferriphoxite is monoclinic, P21/c, with a = 11.389(5), b = 6.352(3), c = 18.716(9), β = 102.887(9)°, V = 1319.8(11) Å3 and Z = 4. Carboferriphoxite is triclinic, P$\bar 1$, with a = 6.4405(3), b = 9.399(5), c = 11.839(6) Å, α = 95.763(10), β = 92.314(10), γ = 100.665(8)°, V = 695.6(6) Å3 and Z = 2. The structures of ferriphoxite (R1 = 0.0678 for 1850 I > 2σI reflections) and carboferriphoxite (R1 = 0.0427 for 3602 I > 2σI reflections) both contain double-strand chains of corner-sharing Fe3+O6 octahedra and PO3(OH) tetrahedra. The chain in ferriphoxite is decorated by PO3OH tetrahedra and C2O4 groups and that in carboferriphoxite is decorated by PO2(OH)2 tetrahedra and C2O4 groups. The interstitial units in both structures contain K+ and NH4+ cations along with a H2O group in ferriphoxite and an H2CO3 group in carboferriphoxite.

Allanite-(Y), ideally CaY(Al2Fe2+)(Si2O7)(SiO4)O(OH), is a valid species with the type locality in the Åskagen pegmatite, Värmland, Sweden. The mineral occurs as an accessory phase in the blocky zone of the NYF granitic pegmatite near Åskagen, Värmland, Sweden. It forms rims together with iimoriite-(Y), gadolinite-(Y) and allanite-(Nd) around altered crystals of thalénite-(Y). Allanite-(Y) replaced primary thalénite-(Y) during an episode of early post-magmatic hydrothermal activity. Allanite-(Y) forms euhedral crystals with size up to 1 mm, black with a vitreous lustre, conchoidal fracture and greyish brown streak. It has a Mohs hardness of ca. 6, the calculated density of 3.945 g.cm–3 and is biaxial (−) with α = 1.760(3), β = 1.799(2) and γ = 1.784(3) in 589 nm light; pleochroism is weak pale yellowish brown in all directions. Allanite-(Y) has monoclinic symmetry, with the space group P21/m, a = 8.8520(8) Å, b = 5.6959(5) Å, c = 10.0543(9) Å, β = 115.510(2)°, V = 457.52(7) Å3 and Z = 2. Crystal-chemical analysis resulted in the empirical formula: A1(Ca0.900Mn0.090Na0.010)Σ1.000A2(Y0.323Ca0.260Nd0.118Sm0.087Gd0.098Dy0.044Ce0.034Pr0.014Tb0.012Er0.005La0.003Ho0.002Yb0.001)Σ1.001M1(Al0.921Fe2+0.070Ti0.003)Σ0.994M2(Al1.000)M3(Fe2+0.638Fe3+0.262Al0.072Mg0.028)Σ1.000T1(Si1.000)T2(Si1.000)T3(Si1.003)O12.000(OH)1.000.

Allanite-(Y) belongs to the allanite group of the epidote supergroup. The closest end-member compositions of valid allanite group species are allanite-(Ce), allanite-(La) and allanite-(Nd) related via the simple exchange mechanism Y ↔ Ln. The allanite-(Y) origin during metasomatic replacement of the thalénite-(Y) was mainly affected by local system composition and structural constraints rather than Ln+Y fluoride complexation in hydrothermal solution.