Whiterockite, CaMgMn3+3O2(PO4)2CO3F·5H2O, is a new phosphate–carbonate mineral from the White Rock No. 2 quarry, Bimbowrie Conservation Park, South Australia, Australia. The mineral is associated with dufrénite/natrodufrénite, ushkovite, bermanite, leucophosphite and sellaite in a matrix comprising fluorapatite and minor quartz. Whiterockite has formed from hydrothermal alteration and weathering in an oxidising, low-temperature and low-pH environment. Whiterockite forms aggregates of thin platy dark-red crystals up to 0.7 mm across with individual crystals up to 0.2 mm in across. Crystals are transparent with a vitreous lustre. The mineral is brittle, has a perfect cleavage on {001} and has an irregular fracture. The measured density is 2.76(2) g/cm–3. Whiterockite is optically biaxial (–), with α = 1.660(3), β = 1.760(5) and γ = 1.770(5), determined in white light; 2Vmeas = 30(1)°; and orientation: X ≈ c*. The mineral is pleochroic: shades of red brown; X < Y < Z. Electron microprobe analyses provided the empirical formula (Ca0.87Na0.18)Σ1.05Mg1.05(Mn3+2.87Fe3+0.10)Σ2.97O1.93(PO4)2.01CO3F1.04·4.99H2O. Whiterockite is monoclinic, C2/m, a = 11.112(2), b = 6.4551(13), c = 10.667(2) Å, β = 102.61(3)º, V = 746.7(3)Å3 and Z = 2. The crystal structure of whiterockite has been refined using single-crystal synchrotron X-ray diffraction data to R1 = 5.10% on the basis of 957 reflections with F0 > 4σ(F0). The structure can be described as a layered structure formed by the stacking along [001] of three kinds of layers and is related to the structure of jörgkellerite.

Manuelarossiite, ideally CaPbAlF7, is a new fluoride mineral found in a specimen from a fumarole formed subsequent to the 1944 eruption of the Vesuvius volcano, Naples Province, Campania, Italy. It occurs as very rare tabular crystals, up to 0.06 × 0.04 × 0.015 mm, in the vugs of volcanic scoria, associated with cerussite. In the same scoria where manuelarossiite was found, anglesite, artroeite, atacamite, calcioaravaipaite, cerussite, challacolloite, cotunnite, hephaistosite, matlockite, napoliite and susannite were identified. Manuelarossiite is colourless with a white streak and adamantine lustre. It is brittle and has a laminated fracture. Cleavage is perfect on {001}. Dcalc = 5.095 g cm–3. The calculated mean refractive index is 1.625. The chemical composition (wt.%, electron microprobe, H2O calculated by stoichiometry) is: CaO 13.98, PbO 55.46, Al2O3 12.59, F 29.45, H2O 1.68, –O=F –12.40, total 100.76. The empirical formula calculated on the basis of 7 anions is Ca1.00Pb1.00Al1.00[F6.25(OH)0.75]Σ7.00. Raman spectroscopy confirms the limited presence of OH– groups in the mineral. Manuelarossiite is monoclinic, space group C2/m, with a = 7.6754(3), b = 7.4443(4), c = 9.2870(5) Å, β = 93.928(5)°, V = 529.39(5) Å3 and Z = 4. The strongest lines of the powder X-ray diffraction pattern [d, Å (I, %) (hkl)] are: 9.257 (57) (001); 4.537 (72) (111); 3.725 (98) (020); 3.630 (57) (20$\bar 1$); 3.588 (65) (11$\bar 2$); 3.460 (100) (021); 3.422 (63) (112); and 2.673 (65) (220). The crystal structure was refined to R1 = 0.056 for 849 reflections with F > 4σ(F). It is characterised by {001} layers formed by CaF8 polyhedra decorated on both sides by AlF6 octahedra, in turn connected to the {001} layer through edge-sharing. Successive {001} layers are bonded through Pb atoms. The new mineral honours Dr. Manuela Rossi (b. 1977) from the University of Naples for her contribution to the study of the Vesuvius volcano and its minerals.

The new mineral pabellóndepicaite (IMA2023-104), Cu2+2(N3C2H2)2(NH3)2(NO3)Cl·2H2O, was found in the guano deposit at Pabellón de Pica, Iquique Province, Chile, where it is a secondary phase formed at the contact between an altered guano deposit and a chalcopyrite-bearing gabbro. Pabellóndepicaite occurs on salammoniac in association with antipinite, bojarite, dittmarite, halite, joanneumite, sampleite, struvite, wheatleyite and whewellite. Crystals are rectangular blades or tablets, up to ∼0.2 mm long, flattened on {001} and elongated along [100] and exhibiting the forms {010}, {001}, {011} and {102}. Crystals are indigo blue and transparent, with vitreous lustre and light indigo blue streak. The mineral is brittle with curved and stepped fracture. The Mohs hardness is ∼2½. Cleavage is perfect on {001} and good on {010}. The density is 1.95(2) g·cm–3. Optically, pabellóndepicaite is biaxial (+) with α = 1.583(3), β = 1.596(3) and γ = 1.644(3) (white light). The 2V is 56(2)° with distinct r > v dispersion. The optical orientation is X = a, Y = b, Z = c and the pleochroism is X light indigo blue, Y indigo blue, Z pale indigo blue; Y > X > Z. The empirical formula is Cu2Cl1.25N9C4H13.75O4.75 (with H, C and N calculated based on the structure). Pabellóndepicaite is orthorhombic, space group Pmma, with cell parameters: a = 7.2118(12), b = 9.0983(15), c = 11.128(3) Å, V = 730.2(2) Å3 and Z = 2. The structure (R1 = 6.65% for 482 I > 2σI reflections) contains two types of polyhedral chains (1) a zig-zag chain of CuN4Cl2 octahedra linked by sharing Cl atoms and the N–N edges of 1,2,4-triazolate groups and (2) a chain of CuN4O2 octahedra alternating with NO3 triangles. The chains are linked to one another by 1,2,4-triazolate groups to form layers with isolated H2O groups in their cavities.

Puttapaite, Pb2Mn2+2ZnCr3+4O2(AsO4)4(OH)6·12H2O, is a new mineral from the Beltana deposit, Puttapa, Flinders Ranges, South Australia, Australia. It forms rosette-like aggregates to 50 micrometers across composed of diamond-shaped tablets to 45 micrometers in length and 5 micrometers in thickness. Crystals are flattened on {001} and the observed forms are {001} and {110}. The calculated density is 3.562 g/cm–3. Optically, puttapaite is biaxial (−) with α = 1.700(5), β = 1.720(5), γ = 1.730(5) and 2V (meas.) = 67(1)°. Electron microprobe analyses gave the empirical formula (based on 36 oxygen atoms pfu) Pb1.96(Mn2+1.52Ca0.28Sr0.22)Σ2.02(Zn0.40Mg0.39Cu0.15)Σ0.94(Cr3+2.89Al0.45Fe3+0.40,Mn3+0.26)Σ4.00O2[(AsO4)3.71(Cr6+O4)0.29]Σ4.00(OH)6.13·11.87H2O. Puttapaite is monoclinic, C2/m, with a = 12.405(3), b = 10.565(2), c = 12.311(3) Å, β = 106.06(3)°, V = 1550.4(6) Å3 and Z = 2.

The structure was solved using synchrotron single-crystal X-ray diffraction data and refined to R1 = 0.1189 on the basis of 915 observed reflections with F0 > 4σ(F0). Puttapaite has a unique structure that consists of M4O16 clusters that share corners with TO4 tetrahedra, which in turn share corners with M1 octahedra in the [010] direction. Clusters link in the [001] direction via corner sharing M2 octahedra to form sheets parallel to {100}. Pb anions lie between the sheets.

Ferriphoxite, [(NH4)2K(H2O)][Fe3+(HPO4)2(C2O4)], and carboferriphoxite, [(NH4)K(H2CO3)][Fe3+(HPO4)(H2PO4)(C2O4)], are new mineral species from the Rowley mine, Maricopa County, Arizona, USA. They occur with antipinite, aphthitalite, baryte, fluorite, hematite and quartz in an unusual bat-guano-related, post-mining assemblage. Ferriphoxite occurs as rectangular blades, up to ∼0.1 mm in length, typically forming sprays. Carboferriphoxite occurs as needles or blades, up to ∼0.2 mm in length, typically forming fan- and bowtie-like sprays. Both species are colourless with white streak, vitreous lustre, ∼2 Mohs hardness, brittle tenacity and splintery fracture. Ferriphoxite has three good cleavages ({100}, {010} and {001}) and carboferriphoxite has two good cleavages (probably {100} and {001}). Both species have a measured density of 2.14(2) g·cm–3. Ferriphoxite is biaxial (+) with α = 1.524(3), β = 1.560(3), γ = 1.608(3) and 2Vmeas. = 83.9(4)°. Carboferriphoxite is biaxial (+) with α = 1.525(3), β = 1.555(calc), γ = 1.630(3) and 2Vmeas. = 67(1)°. Electron probe microanalysis gave {[(NH4)2.13K0.87]Σ3.00(H2O)} {(Fe3+0.95Al0.05)Σ1.00(HPO4)2(C2O4)} for ferriphoxite and {[(NH4)1.12K0.88]Σ2.00(H2CO3)} {(Fe3+0.78Al0.22)Σ1.00(HPO4)(H2PO4)(C2O4)} for carboferriphoxite. Ferriphoxite is monoclinic, P21/c, with a = 11.389(5), b = 6.352(3), c = 18.716(9), β = 102.887(9)°, V = 1319.8(11) Å3 and Z = 4. Carboferriphoxite is triclinic, P$\bar 1$, with a = 6.4405(3), b = 9.399(5), c = 11.839(6) Å, α = 95.763(10), β = 92.314(10), γ = 100.665(8)°, V = 695.6(6) Å3 and Z = 2. The structures of ferriphoxite (R1 = 0.0678 for 1850 I > 2σI reflections) and carboferriphoxite (R1 = 0.0427 for 3602 I > 2σI reflections) both contain double-strand chains of corner-sharing Fe3+O6 octahedra and PO3(OH) tetrahedra. The chain in ferriphoxite is decorated by PO3OH tetrahedra and C2O4 groups and that in carboferriphoxite is decorated by PO2(OH)2 tetrahedra and C2O4 groups. The interstitial units in both structures contain K+ and NH4+ cations along with a H2O group in ferriphoxite and an H2CO3 group in carboferriphoxite.

Allanite-(Y), ideally CaY(Al2Fe2+)(Si2O7)(SiO4)O(OH), is a valid species with the type locality in the Åskagen pegmatite, Värmland, Sweden. The mineral occurs as an accessory phase in the blocky zone of the NYF granitic pegmatite near Åskagen, Värmland, Sweden. It forms rims together with iimoriite-(Y), gadolinite-(Y) and allanite-(Nd) around altered crystals of thalénite-(Y). Allanite-(Y) replaced primary thalénite-(Y) during an episode of early post-magmatic hydrothermal activity. Allanite-(Y) forms euhedral crystals with size up to 1 mm, black with a vitreous lustre, conchoidal fracture and greyish brown streak. It has a Mohs hardness of ca. 6, the calculated density of 3.945 g.cm–3 and is biaxial (−) with α = 1.760(3), β = 1.799(2) and γ = 1.784(3) in 589 nm light; pleochroism is weak pale yellowish brown in all directions. Allanite-(Y) has monoclinic symmetry, with the space group P21/m, a = 8.8520(8) Å, b = 5.6959(5) Å, c = 10.0543(9) Å, β = 115.510(2)°, V = 457.52(7) Å3 and Z = 2. Crystal-chemical analysis resulted in the empirical formula: A1(Ca0.900Mn0.090Na0.010)Σ1.000A2(Y0.323Ca0.260Nd0.118Sm0.087Gd0.098Dy0.044Ce0.034Pr0.014Tb0.012Er0.005La0.003Ho0.002Yb0.001)Σ1.001M1(Al0.921Fe2+0.070Ti0.003)Σ0.994M2(Al1.000)M3(Fe2+0.638Fe3+0.262Al0.072Mg0.028)Σ1.000T1(Si1.000)T2(Si1.000)T3(Si1.003)O12.000(OH)1.000.

Allanite-(Y) belongs to the allanite group of the epidote supergroup. The closest end-member compositions of valid allanite group species are allanite-(Ce), allanite-(La) and allanite-(Nd) related via the simple exchange mechanism Y ↔ Ln. The allanite-(Y) origin during metasomatic replacement of the thalénite-(Y) was mainly affected by local system composition and structural constraints rather than Ln+Y fluoride complexation in hydrothermal solution.