A cation-exchange capacity (CEC) method based on ion-sieving properties was developed for the quantitative determination of clinoptilolite in soils. In this method, both zeolitic and non-zeolitic exchange sites in the soil sample are saturated with Na+. The CEC of the non-zeolitic exchange sites is determined by replacing the Na− in these sites with tert-butylammonium ions. The tert-butylammonium ion cannot be exchanged into the zeolitic exchange sites because it is too large to pass through the channels in the clinoptilolite structure. The sample is next washed with NH4OAc to replace the Na+ in the zeolitic exchange sites. The amount of soil zeolite is then estimated by comparing the CEC of zeolitic exchange sites to the total zeolite CEC (175 meq/100 g for pure clinoptilolite). Prior to the CEC analyses, carbonates and organic matter must be removed to minimize interference with the exchange process. A high correlation (r2 = .96) was observed between the abundance of clinoptilolite estimated using the CEC method and the abundance estimated by semiquantitative X-ray powder diffraction analysis.

The CEC procedure was used to quantify clinoptilolite in an Aridic Calciustoll soil from south Texas. About 2–5% clinoptilolite occurs in the A and B horizons, and concentrations progressively increase with soil depth to as much as 20% in the CBk2 horizon.

Dimethylselenoxide (DMSeO) forms three structurally resolvable intercalates with kaolinite (d(001) = 10.95, 11.26, and 11.38 Å). The 11.26-Å kaolinite: DMSeO intercalate is structurally analogous to the 3-D ordered kaolinite: DMSO intercalate (d(001) = 11.22 Å). Infrared and solid-state 77Se nuclear magnetic resonance data indicate that all DMSeO molecules are equivalent in the structure and, therefore, that the 11.26-Å kaolinite: DMSeO intercalate structure is C-face centered. Structural model refinement from X-ray powder diffraction (XRD) data further support this conclusion (Pl, a = 5.195(2), b = 8.990(4), c = 11.946(5) Å, α = 91.33(2)°, β = 109.39(2)°, γ = 89.77(2)°). The kaolinite: DMSO intercalate structure was subsequently re-refined from the XRD profile in C-face centered Pl. The derived orientation of the DMSO and DMSeO molecules with respect to the basal plane of their respective intercalates is in agreement with polarized infrared measurements of the angles with ab of S=O (40.3°) and Se=O (38.8°) for the 11.26-Å intercalate. The locations of the organic molecules also agree with observed infrared band splittings and perturbations. Interatomic distances calculated from the band shifts agree with those for the XRD derived structures.

The 11.38-Å kaolinite: DMSeO intercalate is closely related to the 11.26-Å intercalate, the main differences being a 2-fold disorder in the orientation of the DMSeO molecule and less penetration of the kaolinite ditrigonal cavity by that molecule. The 10.95-Å kaolinite: DMSeO intercalate, displaying disorder parallel to [110], was obtained from the 11.26- or 11.38-Å intercalates by removal of some DMSeO.

Changes in hydraulic conductivity of smectite-sand mixtures (using four reference smectites) as a function of the concentration (0.01, 0.003, 0.002, 0.001 M Cl- and distilled water) and potassium adsorption ratio (of 2, 4, and 6) of the percolating solution were measured. Swelling and dispersion of the clays were evaluated from the changes in hydraulic conductivity of the mixture and from the clay concentration in the effluent.

The effect of exchangeable potassium percentage (EPP) on the hydraulic conductivity of the smectites depended on the charge density of the clays. The effect of potassium at EPPs <20 on the hydraulic conductivity of smectites having high charge density was negligible. Conversely, the hydraulic conductivity of smectites having low charge density (smectites from Wyoming and Belle Fourche, South Dakota), changed markedly when leached with dilute solutions as the EPP of the clay increased. The dispersive effect of exchangeable potassium on low-charge smectites was similar to that of exchangeable sodium. The low hydration energy of the K+ cations, coupled with the strong electrostatic attraction forces between platelets of smectites with high charge density account for the “inefficiency” of K+ in dispersing these smectites.

Infrared spectra of 2-ethoxyethanol (ethylene glycol monoethyl ether, EGME) adsorbed on Camontmorillonite were obtained using diffuse-reflectance infrared-Fourier-transform (DRIFT) and attenuated total-reflectance (ATR) spectroscopy. The molecular conformation of adsorbed EGME shows predominantly a gauche configuration for the CH2-CH2 linkage as originally present in the liquid. The orientation of the adsorbed EGME molecule in the interlamellar region of the clay was deduced from measurements of the polarized ATR spectra. The planar zig-zag skeleton of the molecule appears to have its long axis tilted at an angle of 44° to the clay surface; the molecule is in van der Waals contact with both adjacent surfaces. Further, the plane of the skeleton of the molecule is tilted at an angle of 69° to the clay surface. This orientation leads to estimates of the d-value of the clay-EGME complex and of the surface area occupied by each molecule. These values are in excellent agreement with independent measurements of both parameters. The full surface coverage on montmorillonite is represented by a single layer of tilted EGME molecules shared by two adjacent clay sheets; each molecule occupies a total surface area consisting of one portion (25.4 Å2) on the lower surface of the interlayer plus another portion (14.8 Å2) on the upper surface. The implication of this model for materials such as kaolinite, where adsorption takes place on the external surface only, is that on these materials each EGME molecule occupies 20 Å2 at full surface coverage.

Imogolite was synthesized at 25°C by aging partially neutralized solutions containing monomeric silicic acid and polymeric hydroxy-aluminum ions for 7 years. Solutions having an initial Si/Al molar ratio of about 0.5 and pHs of 4.0–4.5 produced the largest yields of imogolite, followed by those having an initial Si/Al ratio of about 1, although imogolite was not the principal product. Electron microscopic examination showed a small amount of imogolite fibers embedded in a noncrystalline gel-like substance. Traces of imogolite were detected in solutions having an initial Si/Al ratio of about 2, but no imogolite was found by electron microscopy in products from solutions having an initial Si/Al ratio of about 4. Only gibbsite formed from solutions having initial Si/Al ratios of <0.27. The diameter of the tubular structural unit of the imogolite produced in these experiments was 23 ± 2Å, close to that of natural imogolite.

The effect of pH on the flocculation-dispersion behavior of noncrystalline aluminum and iron oxides, kaolinite, montmorillonite, and various mixtures of these materials was investigated. The clays were Na- or Ca-saturated and freeze-dried before use. Critical coagulation concentrations (CCC) of all materials and mixtures were found to be pH dependent. The Al oxide was flocculated at pH >9.5 and the iron oxide was flocculated between pH 6.0 and 8.2; i.e., flocculation occurred at pHs near the point of zero charge (PZC). The CCC of both the Na- and Ca-clay systems increased with increasing pH. The effect of pH was greater for the Na-kaolinite (flocculated at pH 5.8 and having a CCC of 55 meq/liter at pH 9.1) than the Na-montmorillonite system (having a CCC of 14 meq/liter at pH 6.4 and a CCC of 28 meq/liter at pH 9.4). A 50/50 mixture of Na-kaolinite and Na-montmorillonite behaved more like montmorillonite (having CCCs of 13 and 33 meq/liter at pH 6.2 and pH 9.0, respectively). The presence of either noncrystalline oxide decreased the CCC over that of the clay(s) alone; the decrease occurred at pHs >7 for Al oxide and at pHs >6.5 for Fe oxide. Aluminum oxide produced a greater decrease in CCC than Fe oxide, especially at pHs >8. The effect of each oxide on CCC was greatest near the PZC, 9.5 and 7.2 for Al and Fe oxide, respectively.

Ca-K.-, Na-K-, and Ca-Na-exchange isotherms on four reference smectites were studied. The electric charge on the four smectites was due predominantly to cationic substitution in the octahedral layer and varied between 90 and 122 meq/g (cmole(+)/kg) clay. The affinity of the clays for K increased with a decrease in the fraction of K in the exchange phase. The selectivity coefficients of the smectites for K increased with an increase in charge density. The effect was similar in the Na-K- and Ca-K-exchange isotherms. Charge densities on the smectites had no effect on the Ca-Na-exchange isotherm. The electrostatic attraction forces between the platelets increased with increase in charge density. The low hydration energy of adsorbed K was apparently not enough to overcome these attraction forces as the charge density on the smectites increased. Equilibrium between the low hydration energy of adsorbed K and the electrostatic attraction energies between the platelets is postulated to explain the results.

Tobermorite, Ca5Si6O16(OH)2·4H2O, is a hydrous calcium silicate that has a layer-type of structure similar to that of the 2:1 clay minerals. In its natural form, tobermorite exhibits little or no exchange for alkali cations; synthetic tobermorites, however, exhibit reversible alkali cation exchange and selective cesium uptake upon a coupled substitution of (Al3+ + Na+) for Si4+. Substituted tobermorites were synthesized using aluminosilicate gels, NaOH, and CaO, in Parr bombs at 175°C for 4 days. Unsubstituted tobermorite was synthesized using quartz and CaO in a Parr bomb at 175°C for 20 hr. Two (Al + Na)-substituted tobermorites showed cation-exchange capacities (CEC) of 77 and 71 meq/100 g, whereas an unsubstituted tobermorite showed a CEC of 12 meq/100 g. The substituted tobermorites exhibited selective Cs exchange from either NaCl or CaCl2 solutions. For example, one substituted tobermorite showed a Cs-exchange coefficient (Kd) of 15,100, whereas unsubstituted tobermorite showed a Kd of only 90 from a 0.02 N CaCl2 solution containing 0.0002 moles/liter CsCl. Exchange isotherms for Na+ ⇋ Cs+ showed that Cs+ is preferred over Na+ throughout the exchange in the (Al + Na)-substituted tobermorites. This group of cation exchangers is expected to find applications in radioactive waste disposal.

Clay fractions of eight vertisols and vertisolic soils from Israel were found to consist principally of a Fe-rich beidellite. Sediment volumes of Na-clay suspensions, obtained in measuring cylinders and read every 24 hr for as long as 720 hr, ranged from 3.8 to 8.4 cm/l00 mg clay and were as much as 19 times larger than corresponding suspensions of Ca-clays. Optical density data for all clay suspensions showed absorption curves typical of smectite. The relative number of platelets per tactoid, calculated from optical density measurements, ranged between 1.4 and 5.4 for the Na-clays and between 7.4 and 14.1 for the Ca-clays. In the Ca-clays, the sediment volume decreased with an increase in the relative number of platelets per tactoid. With increase in the major dimension of particles (calculated also from optical density curves), sediment volume tended to increase for the Na-clays and decrease for the Ca-clays. These relationships can be explained on the basis of particle arrangement patterns: face-to-face arrangements dominated the Ca-clays and edge-to-edge and edge-to-face arrangements dominated the Na-clays. The amount of iron extractable in dithionite-citrate-bicarbonate (DCB) correlated positively with the relative number of plates per tactoid and with the major dimensions of the particles in the Ca-clay suspensions. This correlation suggests that DCB-extractable iron affects the tactoid dimensions of Ca-clays from vertisols and, therefore, may also affect structural properties of vertisols.

Optically active cationic complexes adsorbed on montmorillonite can be used for the resolution of racemic mixtures. Montmorillonite-Cu-lysine systems were used as a solid phase in high-pressure liquid chromatography for the resolution of the optical isomers of α-amino acids. Selectivity constants > 1.5 were measured for phenylalanine and tryptophan. The selectivity constants for the amino acids containing saturated-hydrocarbon side chains were in the range of 1.25–1.44. The montmorillonite-Cu-l-lysine complex displayed a stronger affinity for the l-isomers of α-amino acids than for the d-isomers at pHs near neutrality. Inasmuch as surface-catalyzed peptide formation on clays has been proposed as a step in chemical evolution, this stronger affinity between the clay-Cu-l-amino acid complex and l-amino acids might have been significant in prebiotic evolution. The mechanism of optical resolution probably involved ligand exchange. Optimizing the choice of the optically active ligands and of the chelating cation in the chiral agent may improve the resolution of the optical isomers.