Surface Topography of Thin Au and Pd Films After Ion Bombardment Studied With STM

Published online by Cambridge University Press:  15 February 2011

K. P. Reimann ,
A. Rehmet ,
W. Bolse  and
U. Geyer
K. P. Reimann
Affiliation:
I. Physikalisches Institut and SFB 345, Universität Göttingen, Bunsenstr. 7-9, 37073 Göttingen, Germany, kreiman@gwdg.de
A. Rehmet
Affiliation:
I. Physikalisches Institut and SFB 345, Universität Göttingen, Bunsenstr. 7-9, 37073 Göttingen, Germany, kreiman@gwdg.de
W. Bolse
Affiliation:
II. Physikalisches Institut and SFB 345, Universität Göttingen, Bunsenstr. 3-5, 37073 Göttingen, Germany.
U. Geyer
Affiliation:
I. Physikalisches Institut and SFB 345, Universität Göttingen, Bunsenstr. 7-9, 37073 Göttingen, Germany, kreiman@gwdg.de
Get access

Abstract

The changes in surface topography of thin metallic films during ion bombardment were investigated with STM. Pd and Au thin films, having defect-free, atomically flat areas over at least 300×300Å2 were bombarded with Ar+, Kr+, Xe+ ions. Ion energies and target temperatures were varied. The roughening after high fluence irradiation shows scaling with a roughness exponent 0.84. For 300 K target temperature we observe, both for Au and Pd, 3 D erosion, for 700 K, on the contrary, layer-by-layer erosion. The differences in erosion morphologies between Au and Pd surfaces are supposed to stem from differences in surface mobility of adatoms.

Information

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 439: Symposium B – Microstructure Evolution During Irradiation , 1996 , 361
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

[1] Michely, Th. and Comsa, G., Nucl. Instr. Meth. B 82, 207 (1993).Google Scholar
[2] Ghaly, M., Averback, R. S., Phys. Rev. Lett. 72, 364 (1994)Google Scholar
[3] Michely, Th., Berichte des Forschungszentrums Jülich 2569; Jülich, Germany, 1991; p. 15.Google Scholar
[4] Behrisch, R., Sputtering by particle bombardment I, Springer, New York, 1981; p. 179, 188, 231Google Scholar
[5] Michely, Th. and Comsa, G., J. Vac. Sci. Technol. B 9, 862 (1991)Google Scholar
[6] Barabdisi, A.-L., Stanley, H. E., Fractal Concepts in Surface Growth, Cambridge University Press, Cambridge, 1995, pp. 301–304 Google Scholar
[7] Wolf, D. E. and Villain, J., Europhys. Lett. 13, 389 (1990), S. Das Sarma and P. Tamborenea, Phys. Rev. Lett. 66, 325 (1991).Google Scholar
[8] the deposited thickness of 50 Å is equal to the Pd erosion depth for a fluence of 1×1016 Ar+cm-2. Assuming a ratio (adatom yield / sputter yield) ≈ 1 (cf. [9]), the amount of deposited atoms equals the amount of adatoms created by a 1×1016 Ar+cm-2 fluence.Google Scholar
[9] Michely, Th. and Teichert, Ch., Phys. Rev. B 50, 11156 (1994)Google Scholar
[10] Reimann, K. P., Rehmet, A., Geyer, U., in preparationGoogle Scholar
[11] Ziegler, J. F. and Biersack, J. P., The Stopping and Range of Ions in Solids, Pergamon, New York 1985, program version 95.4Google Scholar