Preparation of thin Film YBa2CU3O6+X Ceramic Superconductors by the Sol-Gel Process

Published online by Cambridge University Press:  28 February 2011

S. Kramer ,
K. Wu  and
G. Kordás
S. Kramer
Affiliation:
Department of Materials Science and Engineering, Ceramics Divisron and Materials Research Laboratory, University of Illinois at Urbana-Champaign
K. Wu
Affiliation:
Department of Materials Science and Engineering, Ceramics Divisron and Materials Research Laboratory, University of Illinois at Urbana-Champaign
G. Kordás
Affiliation:
Department of Materials Science and Engineering, Ceramics Divisron and Materials Research Laboratory, University of Illinois at Urbana-Champaign
Get access

Abstract

High Tc superconducting powders and thin films on silicon have been fabricated by the sol-gel process. Both powder and film preparation involved the synthesis of metal alkoxides, followed by the complexation of yttrium, barium, and copper alkoxides in a common solvent. Bulk gels were then vacuum dried and fired at 700 and 950 °C in flowing oxygen. Thin films on (100) silicon were fired at 700 °C in flowing oxygen. Susceptibility vs temperature measurements showed that the thin films on silicon had a Tc of 40 K while the bulk gels fired under the same conditions had a Tc of 75 K. The sample fired at 950 °C was superconducting at 90 K.

Information

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 99: Symposium AA – High-Temperature Superconductors , 1987 , 323
Copyright
Copyright © Materials Research Society 1988

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1. Bednorz, J. G. and Muller, K. A., Z. Phys. B. 64, 189 (1986).Google Scholar
2. Chu, C. W., Hor, P. H., Meng, R. L., Gao, L., Haang, Z. J. and Wang, Y. Q., Phys. Rev. Lett. 58, 405 (1987).Google Scholar
3. Sakka, S., Treatise on Material Science and Technology, Eds. Tomocawa, M. and Doremus, R. H., Vol. 22 Glass III, p. 129.Google Scholar
4. Kramer, S., Wu, K., and Kordas, G., J. Elet. Met, in press.Google Scholar
5. Webb, C., Weng, S. L., Eckstein, J. N., Missert, N., Char, K., Schlom, D. G., Hellman, E. S., and Beasley, M. R., Appl. Phys. Lett. 51, 1191 (1987).Google Scholar
6. Tsaur, B. Y. and Metze, G. M., Appl. Phy. Lett. 45, 535 (1984).Google Scholar
7. Kroemer, H. B., Proc. Mater. Res. Soc. 67, 3 (1986).Google Scholar
8. Lee, J. W., Schichijo, H., Tsai, H. L., and Matyi, R. J., Appl. Phys. Lett. 50, 31, (1987).Google Scholar