Influence of Microstructure on the Corrosion Behavior of a Ni-Si Alloy

Published online by Cambridge University Press:  21 February 2011

P. Kumar
P. Kumar*
Affiliation:
Cabot Corporation, P. O. Box 1296, Reading, PA 19603
Get access

Abstract

Nickel-based alloys with over 7 percent silicon have excellent corrosion resistance to sulfuric acid, oleum and sulfate-ion-containing environments. This alloy is characterized by the presence of intermetallic Ni3Si (beta) and Ni5Si2 (gamma) phases in Ni-Si solid solution (alpha) matrix. The corrosion resistance is provided by the coarse intermetallic phases. Size of intermetallic phases is dependent on the processing condition and the heat treatment. The corrosion resistance can be changed by heat treatment.

Results of corrosion tests are explained in terms of microstructural features.

Information

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 39: Symposium G – High-Temperature Ordered Intermetallic Alloys I , 1984 , 537
Copyright
Copyright © Materials Research Society 1985

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1. Badger, F. S., “Industrial Engineering Chemical,” 1608, 50, 1958.Google Scholar
2. Rabald, E., “Corrosion Guide,” 83, 1968, Publisher: Elseirer, Amsterdam.Google Scholar
3. McClain, G. E., and Muller, W. A., “Corrosion Problem in Acid Flow Control,” Chemical Engineering Processing, 48, Feb. 1982.Google Scholar
4. Barker, W., Evans, T. E., and Williams, K. J., “Effects of Alloying Additions on the Microstructure, Corrosion Resistance and Mechanical Properties of Nickel-Silicon Alloys,” British Corrosion Journal, 76–86, 5, March 1970.CrossRefGoogle Scholar
5. “H ASTELLOY alloy G,” Publ. No. F-30,267D, Cabot Corporation, Kokomo, Indiana.Google Scholar
6. “HASTELLOY alloy C-276,” Publ. No. H-2002, Cabot Corporation, Kokomo, Indiana.Google Scholar
7. Collins, H. H., “Silicon-Ilron Alloys,” 3.98, Corrosion, 1, Editor: Shreir, L. L., Publisher: George Newner Ltd., 1963.Google Scholar
8. “HASTELLOY alloy D,” Publ. No. F-30, 127B, Cabot Corporation, Kokomo, Indiana, 1970.Google Scholar
9. Weisert, E. D., Corrosion, 659, 13, 1957.Google Scholar
10. Soltesz, S. M., “Structure-Property Relationships of Ni-Si-Cu Alloys,” M. S. Thesis, Michigan Technological University, 1982.Google Scholar
11. Lumiden, J. B., and Stocker, P. J., “Properties of the Protective Film on High Silicon Iron,” in Corrosion and Corrosion Protection, Vol.81–8, Editors: Frankenthan, R. P. and Manifield, F., Publisher: The Electrochemical Society, 1981.Google Scholar
12. Enterlein, G., and Feller, H. G., “Investigation of Anodic Dissolution of Nickel-Silicon Alloys,“ Z. Metallkude, 611, 10, 66, 1975.Google Scholar
13. Blondeau, G., Froelicher, M., Froment, M., Hugot-LeGoff, A., and Vignaud, C., “Growth of Oxide Films During the Anodic Polarization of Ni-Si Alloys in H2 S04 Solution,” C. R. Acad. Sci., 407–20, 9, March 1976.Google Scholar
14. U. S. Patent 3311470, Inco.Google Scholar
15. Evans, T.S., and Hart, A.C., “Corrosion and Passivation of a Nickel-Silicon-Base Alloy in Sulfuric Acid Solution,” Electrochemica Acta, 1955–70, 16, 1971.Google Scholar
16. “Metallography, Structures and Phase Diagrams,” p. 325, Metals Handbook Vol.8. Published by American Society for Metals, 1973.Google Scholar
17. “Corrosion Resistance of HASTELLOY Alloys,” Publ. No. H-2000, Cabot Corporation, Kokomo, Indiana.Google Scholar
18. “Oxidation of Metals and Alloys,” Published by American Society for Metals, 1971.Google Scholar
19. Barker, W., Williams, K. J., and Evans, T. E., “New Ni/Si Base Alloy for Sulfuric Acid,” Chemical and Process Engineering, 57–70, September 1970.Google Scholar
20. Rastogi, P. K., and Ardell, A. J., “The Coarsening Behavior of y precipitate in Nickel-Silicon Alloys,” Acta Metallurgica, 321–30, 19, April 1971.Google Scholar