Effect Of Ceramic Dispersoids On The High Temperature Strength Of Mechanically Alloyed MoSi2

Published online by Cambridge University Press:  26 February 2011

Y.S. Kim ,
M.R. Johnson ,
R. Abbaschian  and
M.J. Kaufman
Y.S. Kim
Affiliation:
Dept. of Materials Science & Engineering, University of Florida, Gainesville, FL 32611
M.R. Johnson
Affiliation:
Dept. of Materials Science & Engineering, University of Florida, Gainesville, FL 32611
R. Abbaschian
Affiliation:
Dept. of Materials Science & Engineering, University of Florida, Gainesville, FL 32611
M.J. Kaufman
Affiliation:
Dept. of Materials Science & Engineering, University of Florida, Gainesville, FL 32611
Get access

Abstract

Mechanical alloying (MA) has been used to synthesize MoSi2 from elemental Mo and Si powders. SiC and A12O3 dispersoids were also incorporated as a means of increasing high temperature strength. After synthesis, the powders were consolidated using vacuum hot pressing. It is shown that the size and volume fraction of porosity increases anomalously with increasing hot pressing temperature over the range 1200 to 1700°C. The strengths of the A12O3 composite are, in most instances, considerably higher than the monolithic material produced under similar conditions.

Information

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 213: Symposium Q – High-Temperature Ordered Intermetallic Alloys IV , 1990 , 839
Copyright
Copyright © Materials Research Society 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1. Cotton, J.D., Kim, Y.S., and Kaufman, M.J., Mat. Sci. Engr. (in press).Google Scholar
2. Carter, D., M.S. Thesis, SiC whisker-reinforced MoSi2, MIT, (1987).Google Scholar
3. Petzoldt, F., Scholz, B., and Kunze, H.-D., Mater. Lett. 5 (1987), p. 280.Google Scholar
4. Koch, C.C., Calvin, O.B., McKamey, C.G., and Scarbrough, J.O., Appl. Phys. Lett. 43 (1983), p. 1017.Google Scholar
5. Schultz, L., in New Materials by Mechanical Alloying, edited by Arzt, E. and Schultz, L., Informationsgesellschaft Verlag, (1988), p. 53.Google Scholar
6. Swain, R.A., Thermodynamics of Solids, (1972), p. 116.Google Scholar
7. Maxwell, W.A., Research Memorandum, National Advisory Committee for Aeronautics, (1952).Google Scholar