Coercivity in nanostructured FeCo-based powders prepared by mechanical alloying

Published online by Cambridge University Press:  26 February 2011

Qi Zeng ,
Ian Baker ,
Virginia McCreary  and
Zhicheng Yan
Qi Zeng
Affiliation:
qi.zeng@dartmouth.edu, Dartmouth College, Thayer School of Engineering, HB8000, Hanover, NH, 03755, United States
Ian Baker
Affiliation:
Ian.Baker@dartmouth.edu, Dartmouth College, Thayer School of Engineering, Hanover, NH, 03755, United States
Virginia McCreary
Affiliation:
vm@2447columbia.edu, Columbia University, Department of Materials Science and Engineering, New York, NY, 10027, United States
Zhicheng Yan
Affiliation:
zcyan@physics.udel.edu, University of Delaware, Department of Physics and Astronomy, Newark, DE, 19716, United States
Get access

Abstract

FeCo-based nanostructured powders were prepared by mechanical alloying and subsequently heat treated in an attempt to reduce their coercivity, HC. Although the powders had grain sizes smaller than the magnetic exchange length, a low HC, as expected from Herzer's model, did not occur. The results of magnetic measurements on dilute and concentrated samples of the powder, as well as measurements of the temperature dependence of the magnetic properties from 10-300 K, indicate that the degree of magnetic interaction between the individual powder particles determines the relatively high HC of 10-20Oe at room temperature.

Keywords

nanostructuremagnetic propertiesmechanical alloying

Information

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 980: Symposium II – Advanced Intermetallic-Based Alloys , 2006 , 0980-II06-09
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

1. Herzer, G., IEEE Trans. Magn., 26, 1397 (1990).10.1109/20.104389Google Scholar
2. Kuhrt, Ch. and Schultz, L., J. Appl. Phys. 71(4), 1896 (1992).Google Scholar
3. Ding, J., Li, Y., Chen, L.F., et al, J. Alloys and Comp., 314, 262 (2001)Google Scholar
4. Raja, M. M., Chattopadhyay, K., Majumdar, B., et al, J. Alloys and Comp., 297, 199 (2000).10.1016/S0925-8388(99)00565-4Google Scholar
5. Shashishekar, B. and Baker, I., Proceedings of the MRS, 788, L3.13.1–7, (2004).Google Scholar
6. Baker, I., Quiller, R. G., Robson, M. and Wu, D., Mat. Res. Soc. Proc., 753, BB.5.48.1 (2003).Google Scholar
7. Huang, M.Q., et al, IEEE Trans. Mag., 37, 22239 (2001).Google Scholar
8. Herzer, G., Scr. Metall. Mater., 33, 1741 (1995).10.1016/0956-716X(95)00397-EGoogle Scholar
9. Comstock, R. L., Introduction to Magnetism and Magnetic Recording, Wiley, Chap. 4, (1999).Google Scholar
10. Kronmüller, H., AIPConf. Proc., 10, 1006 (1973).Google Scholar
11. Chen, C.W., Magnetism and Metallurgy of Soft Magnetic Materials, P 132 (1977).10.1016/B978-0-7204-0706-8.50012-5Google Scholar
12. De Toro, J. A. et al., Phy. Rev. B, 73, 094449 (2006).Google Scholar
13. Gangopadhhyay, Y., Hadjipanayis, G. C., Dale, B., et al., Phy. Rev. B, 45, 9778 (1992)10.1103/PhysRevB.45.9778Google Scholar
14. Herzer, G., J. Magn. Magn. Mater., 112, 258 (1992).Google Scholar
15. Mager, A., Ann. Phys. (Leipzig) 6F.11, 15 (1952).Google Scholar
16. Couderchon, G. and Thiers, J. F., J. Magn. Magn. Mater., 26, 196 (1982).10.1016/0304-8853(82)90152-4Google Scholar
17. Néel, L., Compt. Rend., 234, 1150 (1947).Google Scholar
18. Kneller, E. F. and Luborsky, F. E., J. Appl. Phys., 34, 656 (1963).10.1063/1.1729324Google Scholar