Annealing of Irreversible Defects in Hydrogenated and Unhydrogenated Amorphous Silicon Thin Films

Published online by Cambridge University Press:  25 February 2011

G. N. Parsons ,
C. Wang  and
G. Lucovsky
G. N. Parsons
Affiliation:
Department of Physics, North Carolina State University, Raleigh, N.C. 27695-8202
C. Wang
Affiliation:
Department of Physics, North Carolina State University, Raleigh, N.C. 27695-8202
G. Lucovsky
Affiliation:
Department of Physics, North Carolina State University, Raleigh, N.C. 27695-8202
Get access

Abstract

We have prepared unhydrogenated and hydrogenated ([H] = 14 at.%) amorphous silicon thin films using magnetron sputtering with substrate temperature, T S = 40°C. After deposition, the films were annealed at temperatures between 150 and 200°C and conductivity was measured as a function of anneal time. We find that for that for both materials, the conductivity changes non-exponentially with annealing time. The characteristic time constant for annealing at 175°C is approximately the same in unhydrogenated films (τ≈100min) as found in films containing 14 atomic % hydrogen (τ≈200min).

Information

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 192: Symposium O – Amorphous Silicon Technology - 1990 , 1990 , 775
Copyright
Copyright © Materials Research Society 1990

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

Staebler, D.L. and Wronski, C.R., Appl.Phys.Lett. 31, 292 (1977).Google Scholar
Kakalios, J., Street, R.A. and Jackson, W.B., Phys Rev. Lett. 59, 1037 (1987).Google Scholar
[3] Street, R.A. and Winer, K., in “Amorphous Silicon Technology - 1989” MRS Proc. vol. 149, 131 (1989).Google Scholar
[4] Parsons, G.N., Wang, C., Williams, M.J. and Lucovsky, G., to appear in Appl.Phys.Lett., May 1990.Google Scholar
[5] Brodsky, M.H., Title, R.S., Weiser, K. and Pettit, G.D., Phys.Rev.B 1, 2632 (1970).Google Scholar
[6] Moustakas, T.D., Anderson, D.A., and Paul, W., Solid State Comm. 23, 155 (1977).Google Scholar
[7] Rudder, R.A., Cook, J.W. Jr. and Lucovsky, G., Appl.Phys.Lett. 45, 887 (1984).Google Scholar