Amorphous Interface Between Crystalline Nickel and Titanium Films

Published online by Cambridge University Press:  26 February 2011

F.J. Walker ,
R.A. Mckee  and
F.A. List
F.J. Walker
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831
R.A. Mckee
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831
F.A. List
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831
Get access

Abstract

Using in situ reflection high energy electron diffraction and x-ray diffraction, the structure and composition of nickel and titanium multilayer films have been studied. The films were evaporated under UHV conditions at rates of.01 to.1 nm/sec. When deposited on an amorphous NiTi film at 70°C, the individual layers of nickel or titanium are polycrystalline and textured with the close-packed planes perpendicular to the growth direction. The interface between the layers is amorphous and about 2 nm thick. X-ray scattering from the crystalline layers indirectly shows the composition of the amorphous interface to be Ni rich.

Information

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 122: Symposium I – Interfacial Structure, Properties, and Design , 1988 , 585
Copyright
Copyright © Materials Research Society 1988

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCE

1. Schwarz, R. B. and Johnson, W. L., Phys. Rev. Lett. 51, 415 1983 CrossRefGoogle Scholar
2. Miedema, A. R., Phillips Tech. Rev. 36, 217 1976 Google Scholar
3. Hood, G. M. and Schultz, R. J., Phil. Mag. 26, 329 1972 Google Scholar
4. Schwarz, R. B., Petrich, R. R., and Saw, C. K., J. Non-Cryst. Solids 76, 281 1985 Google Scholar
5. Clemens, B. M., Phys. Rev. B33, 7615 1986 Google Scholar
6. Schröder, H., Samwer, K., and Köster, U., Phys. Rev. Lett. 54, 197 1985 Google Scholar
7. Alexander, K. B., Walker, F. J., McKee, R. A., and List, F. A., to be published.Google Scholar